Large enhancement of the thermopower in NaxCoO2 at high Na doping

Research on the oxide perovskites has uncovered electronic properties that are strikingly enhanced compared with those in conventional metals. Examples are the high critical temperatures of the cuprate superconductors and the colossal magnetoresistance in the manganites. The conducting layered cobaltate NaxCoO2 exhibits several interesting electronic phases as the Na content x is varied1,2,3,4, including water-induced superconductivity4 and an insulating state3 that is destroyed by field5. Initial measurements1 showed that, in the as-grown composition, NaxCoO2 has moderately large thermopower S and conductivity σ. However, the prospects for thermoelectric cooling applications faded when the figure of merit Z was found to be small at this composition (0.60.75, S undergoes an even steeper enhancement. At the critical doping xp∼0.85, Z (at 80 K) reaches values ∼40 times larger than in the as-grown crystals. We discuss prospects for low-temperature thermoelectric applications.