High-pressure synthesis of MgB2 with addition of Ti

Abstract Magnesium diboride-based material high-pressure synthesized at 2 GPa and 800 °C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB 2 ) with addition of 2–10 wt.% of Ti demonstrated the critical current density ( j c ) higher than 100 kA/cm 2 at 20 K up to 3 T and at 33 K in 0 T field. At 20 K the critical current density higher than 10 kA/cm 2 was observed up to 5 T field. In the magnetic fields up to 2 T high-pressure synthesized MgB 2 (with 10% of Ti) at 20 K has a critical current density comparable to that of Nb 3 Sn at 4.2 K. XRD patterns of magnesium diboride with Ti addition exhibited no evidence of unreacted titanium and only one compound with titanium was identified, namely, titanium dihydride TiH 2 (or more strictly TiH 1.924 ). The sample with the highest critical current density and the irreversibility field in the temperature range of 25–10 K contained some amount of rather homogeneously dispersed pure Mg and high amount of Mg–B inclusions.