Effect of Mg and C contents in MgCNi3, and structure and superconductivity of MgCNi3-x-Cox

The effect of Mg and C contents on TC in MgCN3, and structure and superconductivity of MgCNi3-xCox were studied. It is found that the excess of Mg and C in initial material mixture is favorable to improvement inTc and helps to obtain single-phase samples. For preparing MgCNi3 superconductor, the optimum composition of starting materials is MgC1.45Ni3 with excess of Mg (20 wt.%) of the stoichiometric composition. In gCNi3-xCox system, a continuous solid solution is formed, lattice parameter decreases slightly andTc decreases obviously with increasingx. A suppression of superconductivity is observed due to the substitution of Co (Mn) for Ni. The suppression effect is smaller for the substitution of Co than that of Mn